Publication database

The laser synthesis and processing of colloids represents a group of scalable and “green” synthesis methods of crystalline metal oxides, that have recently made encouraging progresses in preparing amorphous as well as defect-rich nanoparticles. The relevant conditions and mechanisms that allow the design of amorphous metal oxides (AMOs) remain unknown. Consequently, in this work the synthesis of Fe-based partially amorphous oxide nanoparticles (NPs) by pulsed laser ablation in water was studied. Furthermore, both laser pulse duration and the number of laser pulse in pulsed laser fragmentation in liquid (LFL) allow a precise control of amorphization of AMOs in water. Hereby, a high-fluence nanosecond-LFL provides a significantly higher amorphization rate, whereas picosecond-LFL always presents minor fractions of crystalline α-Fe even with a higher specific energy input and laser intensity. Consequently, the laser fluence required for the repeated melting and quenching of NP appears to be the decisive parameter to control amorphization. During laser synthesis and processing of colloids, the amorphization of AMOs appears to be linked to the apparent size reduction effect, while a complete full amorphization of AMOs may be attributed to the stronger oxidation effects. This work will stimulate future studies using laser-generated AMO NPs for further functional purposes.

Photopolymerization by four-beam interference lithography on a preheated SZ2080 sample was explored at different initial temperatures of the sample: 20 °C, 50 °C, 75 °C, 100 °C, 125 °C, and 150 °C, and at exposure times ranging from 0.5 s to 5 s. The average laser power selected was ∼100 mW for the 300 ps duration pulses at a 1 kHz repetition rate. The experimental results demonstrate that the higher initial temperature of the sample positively influences the crosslinking of the patterns. These findings will improve polymerization protocols for multi-beam interference lithography.

In this paper the possibility to optimize the glass dicing process by controlling the axicon-generated Bessel beam ellipticity is presented. Single-shot intra-volume modifications in soda-lime glass followed by dicing experiments of 1 mm-thick samples are performed. The Bessel beam ellipticity is essential for glass dicing process. Such beam generates intra-volume modifications with transverse crack propagation in dominant direction. Orientation of these modifications parallel to the dicing direction gives significant advantages in terms of processing speed, glass breaking force and cutting quality.

Bio-inspired surfaces are able to decrease friction with fluids and gases. The most recognizable are shark-skin-like riblet surface structures. Such bio-inspired surfaces can be formed by the laser ablation technique. In this work, bio-inspired riblet surfaces with grooves were formed using picosecond ultraviolet laser ablation on pre-heated polytetrafluoroethylene (PTFE) at various sample temperatures. The ablation of hot PTFE was found to be 30% more efficient than the conventional laser structuring at the room temperature. The friction of structured PTFE surfaces with the flowing air was investigated by using drag a measurement setup. Results show the decrease of friction force by 6% with dimensionless riblet spacing around 14–20.

The optical performance of high-resistivity silicon with a laser-ablated surface was studied in the transmission mode in the frequency range of 0.1-4.7 THz. A reciprocal relationship between the transmission brightness and the surface roughness was observed at discrete THz frequencies. The measured dispersion was reproduced by the THz wave scattering theory using an effective refractive index model. No significant differences between the samples processed either with psor ns-duration laser pulses in ambient air or in argon enriched atmosphere were found in the THz regime. It was demonstrated that the majority of optical losses of the silicon with the laser modified surface were due to the scattering of THz waves and not due to the absorption in silicon-compounds formed during the laser ablation.

Results of in-depth experimental analysis of the laser-assisted local copper deposition on commercial Polyamide 6 (PA 6) are presented. Pico- and nanosecond lasers were validated for surface modification of the polymer followed by silver (I) activation and finished by autocatalytic electroless copper plating on the laser-modified areas. Detailed investigations were dedicated to finding out the origin of selective metal plating, including the surface profiling and wettability dynamics, XPS analysis and electric resistance measurements of the deposited copper layer. Based on the experimental data, the mechanism of the polymer surface activation by the laser modification is proposed.

Three different experiments were performed in order to determine the mechanism of pillars formation using four-beam interference lithography. The experimental results demonstrate that pillars, fabricated in argon gas, were wider and higher compared with the pillars fabricated in nitrogen gas, low vacuum or air. It clearly indicates that the pillar bottom widening effect is not affected by the depletion of atmospheric oxygen as in all environments the fabricated pillars have a wider bottom part. Moreover, the shape of the fabricated pillars is not affecting by the back reflection from the positioning stage and by the light irradiation conditions. These results clearly indicate that the photopolymerization process is enhanced by the heat current and it determines the pillar bottom widening effect.

Although nanoporous Pt film has been shown to be an effective catalyst for polymer electrolyte membrane (PEM) fuel cells, the maximum power density of the cell is limited by the optimal film thickness. When the Pt film thickness exceeds the optimal value, regions with good gas transport (the side near the gas diffusion layer (GDL)) separate from regions with good proton transport (the side near the PEM), so the current density and the power density drop with increasing film thickness. Here we demonstrate that this obstacle can be overcome by laser micro-machining the GDL. The picosecond laser fabricates grooves on the GDL surface to greatly increase the effective surface area for Pt deposition, thereby reducing the local Pt film thickness. A nearly two-fold increase in the power density is achieved by using laser micro-machined periodic grooves of 20 μm depth, reaching a 0.6-V power density of 853 mW cm⁻² and a maximum power density of 1.2 W cm⁻² with a cathode Pt loading of 200 μg cm⁻². The results also indicate that further enhancement may be achieved by increasing the surface modulation depth/period ratio and by implementing a better way to fill the grooves with polymer electrolyte.

Solid-state lasers with pulse duration of 10 ps and radiation wavelength of 1064 nm were used to investigate the laser ablation efficiency dependence on processing parameters: laser fluence (pulse energy and beam spot size), beam scanning speed, pulse repetition rate, and scanned line (hatch) distance for the copper sample. Utilising a 40 W power laser, the highest ablation efficiency of 2.5 µm³/µJ and the ablation rate of 100 µm³/µs with the smallest surface roughness of 0.2 µm was obtained. Three-dimensional (3D) fabrication using a galvanometer scanner and layer-by-layer removal technique with optimal parameters defined for efficient ablation were demonstrated at a rate of 6 mm³/min. Combination of high material removal rate with excellent quality and complex 3D structure formation is in a high interest for mimicking bio-inspired surfaces, micro-mould fabrication and decorative applications.

In this paper, we investigate the local oxidation of titanium thin films under the action of picosecond laser pulses. Periodical structures were recorded by the multi-beam interference scheme utilizing various numbers of laser beams, and the relationship between spatial resolution and the contrast of the structures was studied. The Raman spectra of the laser processing regions confirmed the oxidation even under the action of a single picosecond pulse. An analytical simulation of titanium film oxidation in the interference field was provided, and obtained results are correlated with the experimental data. The results of theoretical modeling show that the thermochemical effects of picosecond laser pulses allow recording periodic structures with a period of 0.65 lines per μm. The demonstrated results are important in the adaptation of technological laser systems for the manufacture of diffractive optical elements.