Publication database
Laser-assisted selective copper deposition on commercial PA6 by catalytic electroless plating – Process and activation mechanism
Results of in-depth experimental analysis of the laser-assisted local copper deposition on commercial Polyamide 6 (PA 6) are presented. Pico- and nanosecond lasers were validated for surface modification of the polymer followed by silver (I) activation and finished by autocatalytic electroless copper plating on the laser-modified areas. Detailed investigations were dedicated to finding out the origin of selective metal plating, including the surface profiling and wettability dynamics, XPS analysis and electric resistance measurements of the deposited copper layer. Based on the experimental data, the mechanism of the polymer surface activation by the laser modification is proposed.
Colour-difference measurement method for evaluation of quality of electrolessly deposited copper on polymer after laser-induced selective activation
In this work a novel colour-difference measurement method for the quality evaluation of copper deposited on a polymer is proposed. Laser-induced selective activation (LISA) was performed onto the surface of the polycarbonate/acrylonitrile butadiene styrene (PC/ABS) polymer by using nanosecond laser irradiation. The laser activated PC/ABS polymer was copper plated by using the electroless copper plating (ECP) procedure. The sheet resistance measured by using a four-point probe technique was found to decrease by the power law with the colour-difference of the sample images after LISA and ECP procedures. The percolation theory of the electrical conductivity of the insulator conductor mixture has been adopted in order to explain the experimental results. The new proposed method was used to determine an optimal set of the laser processing parameters for best plating conditions.
Laser-induced selective copper plating of polypropylene surface
Laser writing for selective plating of electro-conductive lines for electronics has several significant advantages, compared to conventional printed circuit board technology. Firstly, this method is faster and cheaper at the prototyping stage. Secondly, material consumption is reduced, because it works selectively. However, the biggest merit of this method is potentiality to produce moulded interconnect device, enabling to create electronics on complex 3D surfaces, thus saving space, materials and cost of production. There are two basic techniques of laser writing for selective plating on plastics: the laser-induced selective activation (LISA) and laser direct structuring (LDS). In the LISA method, pure plastics without any dopant (filler) can be used. In the LDS method, special fillers are mixed in the polymer matrix. These fillers are activated during laser writing process, and, in the next processing step, the laser modified area can be selectively plated with metals.
In this work, both methods of the laser writing for the selective plating of polymers were investigated and compared. For LDS approach, new material: polypropylene with carbon-based additives was tested using picosecond and nanosecond laser pulses. Different laser processing parameters (laser pulse energy, scanning speed, the number of scans, pulse durations, wavelength and overlapping of scanned lines) were applied in order to find out the optimal regime of activation. Areal selectivity tests showed a high plating resolution. The narrowest width of a copper-plated line was less than 23 μm. Finally, our material was applied to the prototype of the electronic circuit board on a 2D surface.