Publication database

The growing demand for flexible, high-quality fabrication of free-form micro-optics drives the development of laser-based fabrication techniques for both the shape formation and surface polishing of optical elements. In this paper, we performed a thorough and systematic study on fused silica glass ablation using 10 ps and 320 fs duration pulses. Ablation processes for both pulse durations were optimized based on the measurements of the removed material layer thickness and surface roughness, and by analyzing the topographies of ablated cavities to remove material layers as thin as possible with minimum surface damage. Our findings demonstrate higher process resolution and surface quality for femtosecond pulses. Ablation of pre-roughened glass reduced the minimal removable glass layer thickness well below the 1 μm mark for both pulse durations, improving the process resolution. The minimal removable glass layer thickness was 14 times smaller for the femtosecond pulses, with up to 4.5 times lower surface roughness compared to samples processed with picosecond pulses. On the other hand, results revealed faster glass removal rates with picosecond pulses. In the end, arrays of microlenses were fabricated with both pulse durations and subsequently polished with a CO2 laser. Results revealed higher performance of microlenses fabricated with femtosecond pulses, providing better focusing capabilities and lesser beam scattering. Finally, this study demonstrated the successful fabrication of free-form optical elements with femtosecond and picosecond pulses, demonstrating the versatility and the potential of laser-based techniques.

Utilisation of high-power ultrafast laser for ablation-based industrial processes such as milling, drilling or cutting requires high production rates and superior quality. In this paper, we demonstrate highly efficient, rapid and high-quality laser micro-machining of three industrial metals (aluminium, copper, and stainless steel). Our proposed optimisation methods of pulse energy division in time result in simultaneous enhancement of ablation efficiency (volume per energy) and ablation rate (volume per time) while maintaining a focused laser beam on the target surface and high resolution. A high-tech femtosecond burst laser, producing laser pulses of τ = 350 fs duration and intra-burst repetition rates of f_P = 50 MHz, was employed in the experiments. Due to the utilisation of bursts, material removal efficiency and removal rate were increased by 18.0 %, 44.5 %, and 37.0 % for aluminium, copper, and stainless steel if compared with the best performance of single-pulses. In addition to the high processing rate, processing by burst mode resulted in lower surface roughness. This technique is believed to be a solution enabling extremely high femtosecond laser powers for precise microfabrication.

Water-assisted ultrashort laser pulse processing of semiconductor materials is a promising technique to diminish heat accumulation and improve process quality. In this study, we investigate femtosecond laser ablation of deep trenches in GaAs, an important optoelectronic material, using water and ambient air environments at different laser processing regimes. We perform a comprehensive analysis of ablated trenches, including surface morphological analysis, atomic-resolution transmission electron microscopy imaging, elemental mapping, photoluminescence, and Raman spectroscopy. The findings demonstrate that GaAs ablation efficiency is enhanced in a water environment while heat-accumulation-related damage is reduced. Raman spectroscopy reveals a decrease in the broad feature associated with amorphous GaAs surface layers during water-assisted laser processing, suggesting that a higher material quality in deep trenches can be achieved using a water environment.

Bio-inspired surfaces are able to decrease friction with fluids and gases. The most recognizable are shark-skin-like riblet surface structures. Such bio-inspired surfaces can be formed by the laser ablation technique. In this work, bio-inspired riblet surfaces with grooves were formed using picosecond ultraviolet laser ablation on pre-heated polytetrafluoroethylene (PTFE) at various sample temperatures. The ablation of hot PTFE was found to be 30% more efficient than the conventional laser structuring at the room temperature. The friction of structured PTFE surfaces with the flowing air was investigated by using drag a measurement setup. Results show the decrease of friction force by 6% with dimensionless riblet spacing around 14–20.

The optical performance of high-resistivity silicon with a laser-ablated surface was studied in the transmission mode in the frequency range of 0.1-4.7 THz. A reciprocal relationship between the transmission brightness and the surface roughness was observed at discrete THz frequencies. The measured dispersion was reproduced by the THz wave scattering theory using an effective refractive index model. No significant differences between the samples processed either with psor ns-duration laser pulses in ambient air or in argon enriched atmosphere were found in the THz regime. It was demonstrated that the majority of optical losses of the silicon with the laser modified surface were due to the scattering of THz waves and not due to the absorption in silicon-compounds formed during the laser ablation.

Solid-state lasers with pulse duration of 10 ps and radiation wavelength of 1064 nm were used to investigate the laser ablation efficiency dependence on processing parameters: laser fluence (pulse energy and beam spot size), beam scanning speed, pulse repetition rate, and scanned line (hatch) distance for the copper sample. Utilising a 40 W power laser, the highest ablation efficiency of 2.5 µm³/µJ and the ablation rate of 100 µm³/µs with the smallest surface roughness of 0.2 µm was obtained. Three-dimensional (3D) fabrication using a galvanometer scanner and layer-by-layer removal technique with optimal parameters defined for efficient ablation were demonstrated at a rate of 6 mm³/min. Combination of high material removal rate with excellent quality and complex 3D structure formation is in a high interest for mimicking bio-inspired surfaces, micro-mould fabrication and decorative applications.

Zone plates with integrated band-pass filters and binary Fresnel lenses designed for the THz spectral range were fabricated by direct laser ablation in metal films and the silicon substrate. Results on the process performance and quality of the products are reviewed. The focusing performance was measured using the THz source that produces the 580 GHz radiation. The beam was directed to the centre of the fabricated optical elements. Zone plates with integrated band-pass filters have shown the double performance in focusing and spectral selection. The dependence of ablation rate and surface roughness on the laser process parameters was thoroughly investigated on the silicon. The depth of the ablated grooves linearly depends on the number of laser scans number with a particular slope for each scanning speed. The process regime with the 125 mm/s scanning speed provided the most precise control over the ablation depth. The topography measurements of the laser fabricated multilevel phase zone plates (Fresnel lenses) with the 10 mm focal length showed good agreement with the calculated topography. The intensity distribution of the focus spots using the laser fabricated 2, 4 and 8 level binary Fresnel lenses showed better focusing performance when more depth levels were applied in the lens production.

As part of a technical challenge under the Advanced Composites Program, methods for improving pre-bond process control for aerospace composite surface treatments and inspections, in conjunction with Federal Aviation Administration guidelines, are under investigation. The overall goal is to demonstrate high fidelity, rapid and reproducible surface treatment and surface characterization methods to reduce uncertainty associated with the bonding process. The desired outcomes are reliable bonded airframe structure, and reduced timeline to certification. In this work, laser ablation was conducted using a q-switched Nd:YVO₄ laser capable of nominal pulse durations of 8 picoseconds (ps). Aerospace structural carbon fiber reinforced composites with an epoxy resin matrix were laser treated, characterized, processed into bonded assemblies and mechanically tested. The characterization of ablated surfaces were conducted using scanning electron microscopy (SEM), water contact angle (WCA) goniometry, micro laser induced breakdown spectroscopy (uLIBS), and electron spin resonance (ESR). The bond performance was assessed using a double cantilever beam (DCB) test with an epoxy adhesive. The surface characteristics and bond performance obtained from picosecond ablated carbon fiber reinforced plastics (CFRPs) are presented herein.

Immune responses have to be tightly controlled to guarantee maintenance of immunological tolerance and efficient clearance of pathogens and tumorigenic cells without induction of unspecific side effects. CD4⁺ CD25⁺ regulatory T cells (Tregs) play an important role in these processes due to their immunosuppressive function. Genetic modification of Tregs would be helpful to understand which molecules and pathways are involved in their function, but currently available methods are limited by time, costs or efficacy. Here, we made use of biofunctionalized gold nanoparticles as non-viral carriers to transport genetic information into murine Tregs. Confocal microscopy and transmission electron microscopy revealed an efficient uptake of the bioconjugates by Tregs. Most importantly, coupling eGFP-siRNA to those particles resulted in a dose and time dependent reduction of up to 50% of eGFP expression in Tregs isolated from Foxp3eGFP reporter mice. Thus, gold particles represent a suitable carrier for efficient import of nucleic acids into murine CD4⁺ CD25⁺ Tregs, superior to electroporation.

This work highlights a strategy for the one-step synthesis of FeAu nanoparticles by the pulsed laser ablation of alloy targets in the presence of different solvents. This method allows particle generation without the use of additional chemicals; hence, solvent-metal interactions could be studied without cross effects from organic surface ligands. A detailed analysis of generated particles via transmission electron microscopy in combination with EDX elemental mapping could conclusively verify that the nature of the used solvent governs the internal phase structure of the formed nanoparticles. In the presence of acetone or methyl methacrylate, a gold shell covering a non-oxidized iron core was formed, whereas in aqueous media, an Au core with an Fe₃O₄ shell was generated. This core-shell morphology was the predominant species found in >90% of the examined nanoparticles. These findings indicate that fundamental chemical interactions between the nanoparticle surface and the solvent significantly contribute to phase segregation and elemental distribution in FeAu nanoparticles. A consecutive analysis of resulting Fe@Au core-shell nanoparticles revealed outstanding oxidation resistance and fair magnetic and optical properties. In particular, the combination of these features with high stability magnetism and plasmonics may create new opportunities for this hybrid material in imaging applications.