Publication database

In this work a novel colour-difference measurement method for the quality evaluation of copper deposited on a polymer is proposed. Laser-induced selective activation (LISA) was performed onto the surface of the polycarbonate/acrylonitrile butadiene styrene (PC/ABS) polymer by using nanosecond laser irradiation. The laser activated PC/ABS polymer was copper plated by using the electroless copper plating (ECP) procedure. The sheet resistance measured by using a four-point probe technique was found to decrease by the power law with the colour-difference of the sample images after LISA and ECP procedures. The percolation theory of the electrical conductivity of the insulator conductor mixture has been adopted in order to explain the experimental results. The new proposed method was used to determine an optimal set of the laser processing parameters for best plating conditions.

Immune responses have to be tightly controlled to guarantee maintenance of immunological tolerance and efficient clearance of pathogens and tumorigenic cells without induction of unspecific side effects. CD4⁺ CD25⁺ regulatory T cells (Tregs) play an important role in these processes due to their immunosuppressive function. Genetic modification of Tregs would be helpful to understand which molecules and pathways are involved in their function, but currently available methods are limited by time, costs or efficacy. Here, we made use of biofunctionalized gold nanoparticles as non-viral carriers to transport genetic information into murine Tregs. Confocal microscopy and transmission electron microscopy revealed an efficient uptake of the bioconjugates by Tregs. Most importantly, coupling eGFP-siRNA to those particles resulted in a dose and time dependent reduction of up to 50% of eGFP expression in Tregs isolated from Foxp3eGFP reporter mice. Thus, gold particles represent a suitable carrier for efficient import of nucleic acids into murine CD4⁺ CD25⁺ Tregs, superior to electroporation.

Laser writing for selective plating of electro-conductive lines for electronics has several significant advantages, compared to conventional printed circuit board technology. Firstly, this method is faster and cheaper at the prototyping stage. Secondly, material consumption is reduced, because it works selectively. However, the biggest merit of this method is potentiality to produce moulded interconnect device, enabling to create electronics on complex 3D surfaces, thus saving space, materials and cost of production. There are two basic techniques of laser writing for selective plating on plastics: the laser-induced selective activation (LISA) and laser direct structuring (LDS). In the LISA method, pure plastics without any dopant (filler) can be used. In the LDS method, special fillers are mixed in the polymer matrix. These fillers are activated during laser writing process, and, in the next processing step, the laser modified area can be selectively plated with metals.

In this work, both methods of the laser writing for the selective plating of polymers were investigated and compared. For LDS approach, new material: polypropylene with carbon-based additives was tested using picosecond and nanosecond laser pulses. Different laser processing parameters (laser pulse energy, scanning speed, the number of scans, pulse durations, wavelength and overlapping of scanned lines) were applied in order to find out the optimal regime of activation. Areal selectivity tests showed a high plating resolution. The narrowest width of a copper-plated line was less than 23 μm. Finally, our material was applied to the prototype of the electronic circuit board on a 2D surface.

Cu-chalcopyrite based solar cells such as Cu(In,Ga)Se₂ (CIGS) have been established as the most efficient thin-film technology in converting sunlight into electricity. Laser scribed monolithic interconnects are one of the key technologies which will play a significant role in future develop-ments of CIGS technology. Laser scribing is needed to maintain module efficiency by dividing large scale device to smaller cells interconnected in series. CIGS layer is a thermally sensitive material, and laser modification can induce local structural changes of the active layer and significantly modi-fy the electrical properties. Therefore, the laser modified region can act as series interconnect be-tween the adjacent cells. In this study, we investigated the laser modification of the CIGS active layer with picosecond laser. The EDS analysis revealed the increase of Cu/(In+Ga) ratio in laser treated areas while Raman measurements indicated changes in main CIGS peak and formation of the Cu-rich CuGaSe₂ phase. Therefore, this resulted in significant electrical conductivity increase in laser-treated areas. Electrical testing of the laser performed P2 micro-welds showed scribe conduc-tivities up to 9.3 Ω·cm which are acceptable for the cell serial interconnection.

This work highlights a strategy for the one-step synthesis of FeAu nanoparticles by the pulsed laser ablation of alloy targets in the presence of different solvents. This method allows particle generation without the use of additional chemicals; hence, solvent-metal interactions could be studied without cross effects from organic surface ligands. A detailed analysis of generated particles via transmission electron microscopy in combination with EDX elemental mapping could conclusively verify that the nature of the used solvent governs the internal phase structure of the formed nanoparticles. In the presence of acetone or methyl methacrylate, a gold shell covering a non-oxidized iron core was formed, whereas in aqueous media, an Au core with an Fe₃O₄ shell was generated. This core-shell morphology was the predominant species found in >90% of the examined nanoparticles. These findings indicate that fundamental chemical interactions between the nanoparticle surface and the solvent significantly contribute to phase segregation and elemental distribution in FeAu nanoparticles. A consecutive analysis of resulting Fe@Au core-shell nanoparticles revealed outstanding oxidation resistance and fair magnetic and optical properties. In particular, the combination of these features with high stability magnetism and plasmonics may create new opportunities for this hybrid material in imaging applications.

Cu-chalcopyrite based solar cells, such as Cu(In,Ga)Se₂ (generally called CIGS) have been established as the most efficient thin-film technology in converting sunlight into electricity. High efficiency, flexibility and small weight make this technology attractive for future developments. Large scale production of these devices requires innovative technological solutions including the laser scribed monolithic interconnects. Laser scribing is needed to maintain module efficiency by dividing large scale device to smaller cells interconnected in series. Serious challenges in laser scribing technology have to be solved, including the laser induced thermal modification of the CIGS absorber layer. CIGS layer is thermally sensitive material, and laser modification can induce local structural changes and phase transitions to the metallic state. That is undesirable for the P3 scribing since superior isolating properties are needed. However, this effect can be used for the P2 process – interconnection of the adjacent cells. In this study, we investigated the picosecond laser modification of the CIGS active layer to form the series interconnect. The P2 laser process was optimized relying on the scribe electrical resistivity measurements with the best value of 3.5 Ω·cm. The EDS analysis revealed the increase of Cu/(Ga + In) ratio in laser treated areas while Raman measurements indicated changes in main CIGS peak and the formation of the Cu-rich CuGaSe₂ phase. Therefore, this resulted in a significant electrical conductivity increase in laser-treated areas which is acceptable for the cell serial interconnection.

New results on development of the Direct Laser Interference Patterning (DLIP) technique using the interference of several beams to directly ablate the material are presented. The method is capable of producing sub-wavelength features not limited by a beam spot size and is an effective method of forming two-dimensional periodic structures on relatively large area with just a single laser shot. Surface texturing speed of DLIP method and the direct laser writing was compared. Fabrication time reduction up to a few orders of magnitude using DLIP was evaluated. The sub-period scanning technique was applied for formation of the complex periodic structures. A new method of laser scanning for fabrication of periodic structures on large areas without any visible stitching signs between laser irradiation spots was tested.

The picosecond laser-induced ripple formation on the stainless steel surface upon irradiation with linearly-polarized single-pulse and dual-wavelength cross-polarized double-pulse trains in air was studied experimentally. The characteristic switching of the ripple period and orientation were observed depending on the inter-pulse delay in the dual-wavelength cross-polarized double-pulse train irradiation experiments.

Hybrid particles are of great significance in terms of their adjustable optical, electronic, magnetic, thermal and mechanical properties. As a novel technique, laser ablation in liquids (LAL) is famous for its precursor-free, “clean” synthesis of hybrid particles with various materials. Till now, almost all the LAL-generated particles originate from the nucleation-growth mechanism. Seed-growth of particles similar to chemical methods seems difficult to be achieved by LAL. Here, we not only present novel patch-joint football-like AgGe microspheres with a diameter in the range of 1 ~ 7 μm achievable by laser ablation in distilled water but also find direct evidences of their layered seed growth mechanism. Many critical factors contribute to the formation of AgGe microspheres: fast laser-generated plasma process provide an excellent condition for generating large amount of Ge and Ag ions/atoms, their initial nucleation and galvanic replacement reaction, while cavitation bubble confinement plays an important role for the increase of AgGe nuclei and subsequent layered growth in water after bubble collapse. Driven by work function difference, Ge acts as nucleation agent for silver during alloy formation. This new seed-growth mechanism for LAL technique opens new opportunities to develop a large variety of novel hybrid materials with controllable properties.