The picosecond laser irradiation of diamond-like carbon (DLC) film on the silicon wasinvestigated. The DLC films were irradiated by Nd:YVO₄ laser with the infrared (1064 nm, fluency 1.02 J/cm²) and ultraviolet (355 nm, fluency 0.79 J/cm²) wavelengths with 1, 10, and 100 pulse numbers per spot. The energy dispersive X-ray spectroscopy and microRaman spectroscopy measurements indicated that the full ablation area of the DLC was narrower than laser beam radius of the 1064 nm wavelength with 10 and 100 pulses. The increase of the oxygen concentration was obtained near the ablation areas after irradiation with the first harmonic. The microRaman and SEM measurements demonstrated that the DLC film was fully ablated in the laser spot when the third harmonic was used. The formation of silicon carbide (SiC) in the center of the irradiated spot was found after 100 pulses.

Hybrid particles are of great significance in terms of their adjustable optical, electronic, magnetic, thermal and mechanical properties. As a novel technique, laser ablation in liquids (LAL) is famous for its precursor-free, “clean” synthesis of hybrid particles with various materials. Till now, almost all the LAL-generated particles originate from the nucleation-growth mechanism. Seed-growth of particles similar to chemical methods seems difficult to be achieved by LAL. Here, we not only present novel patch-joint football-like AgGe microspheres with a diameter in the range of 1 ~ 7 μm achievable by laser ablation in distilled water but also find direct evidences of their layered seed growth mechanism. Many critical factors contribute to the formation of AgGe microspheres: fast laser-generated plasma process provide an excellent condition for generating large amount of Ge and Ag ions/atoms, their initial nucleation and galvanic replacement reaction, while cavitation bubble confinement plays an important role for the increase of AgGe nuclei and subsequent layered growth in water after bubble collapse. Driven by work function difference, Ge acts as nucleation agent for silver during alloy formation. This new seed-growth mechanism for LAL technique opens new opportunities to develop a large variety of novel hybrid materials with controllable properties.